AL2O3 Electronic Ceramic Components
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Name | Electronic Ceramic Components / Electronic Ceramics | AL2O3 Content | 90% - 99% |
---|---|---|---|
Tensile | 30 Kpsi - 32 Kpsi | Flexural | 55 Kpsi - 60 Kpsi |
Compressive | 300 Kpsi - 330 Kpsi | Density | 3.7 G/cc - 3.92 G/cc |
Hardness | 13.8 HV, Gpa - 18 HV, Gpa | Thermal Conductivity | 25 W/(m K) - 32 W/(m K) |
C.O.T.E | 75 In / In°C (x10^7) - 78 In / In°C (x10^7) | Working Temperature | 1500 °C - 1750 °C |
Dielectric Constant | 9.5 - 9.8 | Volume Resistivity | >10^14 Ohm-cm |
Dielectric Strength | 16 KV/mm - 20 KV/mm | ||
High Light | AL2O3 Electronic Ceramic Components,wear resistant Electronic Ceramic Components,AL2O3 advanced structural ceramics |
Electronic Ceramic Components / Ceramic Electronic Parts
1. Description:
Market research conducted in 1998 by the Japan Technology Transfer Association clarified that the actual demands for actuators are: 100 μm displacement, 100 N force and 100 μs response. Because neither the multilayer nor the bimorph can satisfy this actual demand, composite actuator structures called the ‘moonie’ and ‘cymbal’ were developed to provide characteristics intermediate between the multilayer and bimorph actuators; this type of transducer has a displacement an order of magnitude larger than the multilayer, and a much larger generative force with a quicker response than the bimorph.73 The device consists of a thin multilayer piezoelectric element and two metal plates with a narrow moon-shaped or cymbal-shaped cavity bonded together as shown in Fig. 3.27. The moonie, with a size of 5 × 5 × 2.5 mm3, can generate a 20 μm displacement under 60 V, eight times as large as the generative displacement produced by a multilayer of the same size.74 This new compact actuator has been used in a miniaturized laser beam scanner.
1) High hardness and high density
2) Low thermal conductivity
3) Chemical inertness
4) Good wear resistance
5) High Fracture toughness
6) Good insulation performance
7) High temperature resistance
8) A variety of specifications is available
9) Satisfy various technical requests
10) Lower medium spoilage
11) Stiffness texture
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
3. Material Features / Properties:
Color | White or Ivory | White or Ivory | White or Ivory | |
Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
Hardness | HRA | 83 | 85 | 85 |
Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
Technical Parameters of Ceramics | ||||||||
Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
Liquid Permeability | -- | -- | Pass | Pass | Pass | Pass | - | |
Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
Poisson Ratio | - | - | - | 0.20~0.25 | 0.20~0.25 | - | - | - |
Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | Pass | Pass | Pass | - | - | - | |
Coefficient of Linear Expansion | 20℃~100℃ | ×10-6 K-1 | - | - | - | ≤8 | - | |
20℃~500℃ | ×10-6 K-1 | 6.5~7.5 | 6.5~7.5 | 6.5~7.5 | 6.5~11.2 | - | - | |
20℃~800℃ | ×10-6 K-1 | 6.5~8.0 | 6.5~8.0 | 6.3~7.3 | - | 4 | ||
20℃~1200℃ | ×10-6 K-1 | - | 7.0~8.5 | - | - | - | - | |
Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90~110 |
1000℃ | ||||||||
Dielectric Constant | 1MHz 20℃ | - | 9.0~10.5 | 9.0~10 | 9.0~10 | - | ≤7.5 | - |
1MHz 50℃ | - | - | 9.0~10 | - | - | - | - | |
10GHz 20℃ | - | 9.0~10.5 | 9.0~10 | 9.0~10 | - | - | - | |
Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - | ||
500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - | ||
Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - | |
Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing
6. Application Fields:
Widely apply for new energy vehicles, charging piles, solar power generation, energy storage and power storage system, electric vehicle power system and so on.
7. Production Facilities: Prilling Tower , Forming Machine , High Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer , Granulometer , Helium Mass Spectrometer Leak Detector , Universal Pull Force Meter
9.Order Flow Steps as belows: Inquiry ---Quotation --- Place an order --- Production --- Delivery
10. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ; Good Service
11.Shipping and Package:
12. Our aimed market :
Notes:Above information only for reference and please contact with us for more details freely when you have any inquiry!