All Products
-
Alumina Ceramic Components
-
Ceramic Housing
-
Metallized Alumina Ceramics
-
Custom Ceramic Parts
-
Alumina Ceramic Insulator
-
Alumina Ceramic Rings
-
Pressure Sensor Ceramic
-
Advanced Technical Ceramics
-
Advanced Engineering Ceramics
-
Fuse Ceramic
-
Ceramic Connector Blocks
-
Electronic Ceramic Components
-
Magnetron Ceramic
-
Zirconia Ceramic Parts
-
Alumina Ceramic Rods
-
Mr.FarnReply very fast and easy to talk! -
Mr.JacksonGood service and nice to talk.
Contact Person :
Alice Deng
Phone Number :
+8615073852630
Insulated Alumina Ceramic Rods Aluminum Oxide Rod Wear Resistant For Battery
| Place of Origin | Hunan,China |
|---|---|
| Brand Name | Antaeus |
| Certification | / |
| Model Number | AD-B012 |
| Minimum Order Quantity | Negotiation |
| Price | Negotiation |
| Packaging Details | Inner vacuum packaging, outside carton. |
| Delivery Time | 15-45 days |
| Payment Terms | T/T or Negotiation |
| Supply Ability | Full Supply |
Contact me for free samples and coupons.
Whatsapp:0086 18588475571
Wechat: 0086 18588475571
Skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Product Name | Alumina Ceramic Rods / Aluminum Oxide Insulation Rods For Battery | AL2O3 Content | 90% - 99% |
|---|---|---|---|
| Tensile | 30 Kpsi - 32 Kpsi | Flexural | 55 Kpsi - 60 Kpsi |
| Compressive | 300 Kpsi - 330 Kpsi | Density | 3.7 G/cc - 3.92 G/cc |
| Hardness | 13.8 HV, Gpa - 18 HV, Gpa | Thermal Conductivity | 25 W/(m K) - 32 W/(m K) |
| C.O.T.E | 75 In / In°C (x10^7) - 78 In / In°C (x10^7) | Working Temperature | 1500 °C - 1750 °C |
| Dielectric Constant | 9.5 - 9.8 | Volume Resistivity | >10^14 Ohm-cm |
| Dielectric Strength | 16 KV/mm - 20 KV/mm | ||
| High Light | Insulated Alumina Ceramic Rods,Wear Resistant Alumina Ceramic Rods,Insulated aluminum oxide rod |
||
Product Description
Alumina Ceramic Rods / Aluminum Oxide Insulation Rods for Battery
1. Description:
Technical ceramics have been used for various parts of the engine for the past 30-40 years, but a lot of activity currently surrounds the development of silicon carbide (SiC/SiC composites) for use in jet engine turbines, mainly concentrated on the turbine blades. The main driver is fuel efficiency, as engineers seek to run the jet engine without the need for cooling channels that currently stop the metal alloy blades from melting. If the blades were made of ceramic composites, which could deal with temperatures of 1,500-1,600°C, the engine could run at higher temperatures. Energy efficiency would therefore increase, which leads to less fuel and the airplane’s ability to fly further or more efficiently.
Feature Advantages:
1) High hardness and high density
2) Low thermal conductivity
3) Chemical inertness
4) Good wear resistance
5) High Fracture toughness
6) Good insulation performance
7) High temperature resistance
8) A variety of specifications is available
9) Satisfy various technical requests
10) Lower medium spoilage
11) Stiffness texture
12) Chemical inertness
13) Good wear resistance
14) High Fracture toughness
15) Good insulation performance
3. Material Features / Properties:
| Color | White or Ivory | White or Ivory | White or Ivory | |
| Density | g/cm 3 | 3.82 | 3.9 | 3.92 |
| Hardness | HRA | 83 | 85 | 85 |
| Flexural Strength | Mpa (psi*10 3 ) | 375 | 386 | 381 |
4. Technical Parameters:
| Technical Parameters of Ceramics | ||||||||
| Items | Test Conditions | Unit or Symbol | 99% AL2O3 | 95% AL2O3 | 90% AL2O3 | Zirconia | Steatite | Silicon Carbide |
| Volume Density | -- | g/cm3 | ≥3.70 | ≥3.62 | ≥3.40 | ≥5.90 | ≥2.60 | ≥3.08 |
| Tightness | -- | Pa·m³/s | ≤1.0×10-11 | ≤1.0×10-11 | ≤1.0×10-11 | - | - | - |
| Liquid Permeability | -- | -- | Pass | Pass | Pass | Pass | - | |
| Flexural Strength | - | MPa | ≥300 | ≥280 | ≥230 | ≥1100 | ≥120 | ≥400 |
| Elastic Modulus | - | GPa | - | ≥280 | ≥250 | ≥220 | - | 400 |
| Poisson Ratio | - | - | - | 0.20～0.25 | 0.20～0.25 | - | - | - |
| Thermal Shock Resistance | 800℃( Room Temperature) Cycle: 10 times | Pass | Pass | Pass | - | - | - | |
| Coefficient of Linear Expansion | 20℃～100℃ | ×10-6 K-1 | - | - | - | ≤8 | - | |
| 20℃～500℃ | ×10-6 K-1 | 6.5～7.5 | 6.5～7.5 | 6.5～7.5 | 6.5～11.2 | - | - | |
| 20℃～800℃ | ×10-6 K-1 | 6.5～8.0 | 6.5～8.0 | 6.3～7.3 | - | 4 | ||
| 20℃～1200℃ | ×10-6 K-1 | - | 7.0～8.5 | - | - | - | - | |
| Coefficient of Thermal Conductivity | 20℃ | W/(m·k) | - | - | - | - | - | 90～110 |
| 1000℃ | ||||||||
| Dielectric Constant | 1MHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | ≤7.5 | - |
| 1MHz 50℃ | - | - | 9.0～10 | - | - | - | - | |
| 10GHz 20℃ | - | 9.0～10.5 | 9.0～10 | 9.0～10 | - | - | - | |
| Volume Resistivity | 100℃ | Ω·cm | ≥1.0×1013 | ≥1.0×1013 | ≥1.0×1013 | - | ≥1.0×1012 | - |
| 300℃ | ≥1.0×1013 | ≥1.0×1010 | ≥1.0×1013 | - | - | - | ||
| 500℃ | ≥1.0×109 | ≥1.0×108 | -- | - | - | - | ||
| Disruptive Strength | D.C | kV/mm | ≥17 | ≥15 | ≥15 | - | ≥20 | - |
| Chemical Durability | 1:9HCl | mg/c㎡ | ≤0.7 | ≤7.0 | - | - | - | - |
| 10%NaOH | mg/c㎡ | ≤0.1 | ≤0.2 | - | -- | - | - | |
| Grain Size | - | μm | - | 3~12 | - | - | - | - |
5. Process Flows:
Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Printing --- Nickel Plating --- Assembing --- Brazing --- Inspecting --- Packing
6. Application Fields:
Widely apply for new energy vehicles, charging piles, solar power generation, energy storage and power storage system, electric vehicle power system and so on.
7. Production Facilities: Prilling Tower , Forming Machine , High Temperature Sintering Kiln
8. Detection Devices:
Electric Performance Tester , Film Thickness Analyzer , Granulometer , Helium Mass Spectrometer Leak Detector , Universal Pull Force Meter
9.Order Flow Steps as belows: Inquiry ---Quotation --- Place an order --- Production --- Delivery
10. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ; Good Service
11.Shipping and Package:
12. Our aimed market :
Notes:Above information only for reference and please contact with us for more details freely when you have any inquiry!
Recommended Products