ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly

Place of Origin Hunan,China
Brand Name Antaeus
Certification /
Model Number AD-A011
Minimum Order Quantity Negotiation
Price Negotiation
Packaging Details Inner vacuum packaging, outside carton.
Delivery Time 15-45 days
Payment Terms T/T or Negotiation
Supply Ability Full Supply

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Chemical Ingredients Al2O3 Max. Use Temp. 1650℃
Bulk Density 3.6g/cm3-3.9g/cm3 Water Absorption 0%
ROHS Hardness ≥85 Flexural Strength 358(52) - 550 Mpa(psix10^3)
Compressive Strength 2068(300) - 2600(377) Mpa(psix10^3) Coefficient Of Thermal Expansion 7.6 - 8.2 / 1X10^-6/℃
Coefficient Of Thermal Conductivity 16-30.4 / W/m.K Thermal Shock Resistance 250℃
Dielectricity Constant 9-9.7 / 1MHz.25℃ Dielectric Strength 8.3(210) - 8.7(220) / Ac-kV/mm(ac V/mil)
Volume Resistivity >10^13 Ohm-cm
High Light

ISO Pressing Alumina Ceramic Components

,

Brazed Assembly Alumina Ceramic Components

,

Ceramic To Metal Brazed Assembly

Leave a Message
Product Description

Alumina ceramic components / relay ceramic assemblies / ceramic - metal brazed contactor

 

1. Description:

1) ISO pressing --- ISO pressing is a forming process where our in house spray dried material is used to fill a mold and then compacted at around 20,000 PSI. ISO pressing is used to create blanks of certain sizes and shapes that cannot be easily formed by dry pressing or the extrusion process. These blanks can then be machined green or in the bisque state.

2) Bisque --- Bisque alumina is material that has been pressed or compacted into shape and then is partially fired. This enables the material to become harder than “green” material but not as hard as fully fired alumina. Bisque firing allows the material to be machined using conventional methods and tooling. Once bisqued, the material has a hard chalky feel to it. Bisque material can be used to create prototypes or one off parts. Once the part is complete, bisque alumina can be fully fired to achieve a harder, fully dense part with all the properties of alumina.

 

2. Feature Advantages:

1) High elasticity modulus

2) High compressive strength.

3) Anti corrosion

4) Abrasion resistance

5) Impact resistance

6) High precision

7) High stability

8) Good advanced ceramic materials

9) High welding sealing performance

10) High hardness and high density

11) Low thermal conductivity

12) Chemical inertness

13) Good wear resistance

14) High Fracture toughness

15) Good insulation performance

16) High temperature resistance

17) A variety of specifications is available

18) Satisfy various technical requests

19) Lower medium spoilage

20) Stiffness texture

21) Widely apply for automotive ceramic sensor , ceramic heater ,electric heating

 

3. Material Features / Properties:

Composite (wt %) 99% 99.5% 99.8%
Color   White or Ivory White or Ivory White or Ivory
Density g/cm 3 3.82 3.9 3.92
Hardness HRA 83 85 85
Flexural Strength Mpa (psi*10 3 ) 375 386 381

 

4. Technical Parameters:

Technical Parameters of Ceramics
Items Test Conditions Unit or Symbol 99% AL2O3 95% AL2O3 90% AL2O3 Zirconia Steatite Silicon Carbide
Volume Density -- g/cm3 ≥3.70 ≥3.62 ≥3.40 ≥5.90 ≥2.60 ≥3.08
Tightness -- Pa·m³/s ≤1.0×10-11 ≤1.0×10-11 ≤1.0×10-11 - - -
Liquid Permeability -- -- Pass Pass Pass   Pass -
Flexural Strength - MPa ≥300 ≥280 ≥230 ≥1100 ≥120 ≥400
Elastic Modulus - GPa - ≥280 ≥250 ≥220 - 400
Poisson Ratio -   - - 0.20~0.25 0.20~0.25 - - -
Thermal Shock Resistance 800℃( Room Temperature) Cycle: 10 times   Pass Pass Pass - - -
Coefficient of Linear Expansion 20℃~100℃ ×10-6 K-1 - - -   ≤8 -
20℃~500℃ ×10-6 K-1 6.5~7.5 6.5~7.5 6.5~7.5 6.5~11.2 - -
20℃~800℃ ×10-6 K-1 6.5~8.0 6.5~8.0 6.3~7.3   - 4
20℃~1200℃ ×10-6 K-1 - 7.0~8.5 - - - -
Coefficient of Thermal Conductivity 20℃ W/(m·k) - - - - - 90~110
1000℃
Dielectric Constant 1MHz 20℃ - 9.0~10.5 9.0~10 9.0~10 - ≤7.5 -
1MHz 50℃ - - 9.0~10 - - - -
10GHz 20℃ - 9.0~10.5 9.0~10 9.0~10 - - -
Volume Resistivity 100℃ Ω·cm ≥1.0×1013 ≥1.0×1013 ≥1.0×1013 - ≥1.0×1012 -
300℃ ≥1.0×1013 ≥1.0×1010 ≥1.0×1013 - - -
500℃ ≥1.0×109 ≥1.0×108 -- - - -
Disruptive Strength D.C kV/mm ≥17 ≥15 ≥15 - ≥20 -
Chemical Durability 1:9HCl mg/c㎡ ≤0.7 ≤7.0 - - - -
10%NaOH mg/c㎡ ≤0.1 ≤0.2 - -- - -
Grain Size - μm - 3~12 - - - -

 

5. Process Flows:

Formulating --- Granulating --- Forming --- Sintering --- Grinding --- Inspecting --- Packing

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 0

 

6. Application Fields:

New energy vehicles, charging piles, solar power generation, energy storage and power storage system, electric vehicle power system and so on.

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 1

 

7. Production Facilities: Prilling Tower , Forming Machine , High Temperature Sintering Kiln

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 2

 

8. Detection Devices:

Electric Performance Tester , Film Thickness Analyzer , Granulometer , Helium Mass Spectrometer Leak Detector , Universal Pull Force Meter

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 3

9. Order Flow Steps as belows: Inquiry ---Quotation --- Place an order --- Production --- Delivery

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 4

 

 

10. Our advantages: Quality Assurance ; Price Competitive ; Factory Supply Directly ; Good Service

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 5

11Shipping and Package:

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 6

12. Our aimed market:

ISO Pressing Alumina Ceramic Components Ceramic To Metal Brazed Assembly 7

 

Notes:Above information only for reference and please contact with us for more details freely when you have any inquiry!